Karakterisasi biokomposit sheep hydroxyapatite (sha)/shellac/tepung terigu

Izmi Mahfudi, Joko Triyono, Teguh Triyono

Abstract

The development of science and technology has led to new inovations in the medical field, especially ortopedic. The aim of those inovations is to find the alternatives of good materials that can replace the broken sturcture of bone tissue. One of the innovations conducted is the characterization of sheep hydroxyapatite biocomposite. This study aims to investigate the mechanical properties of the material Sheep Hydroxyapatite (SHA) / shellac / wheat fluor. Sheep bone powder already gained from the crusher process and meshing into size of 100 and are soaked for 24 hours, then mixed with wheat flour with the ratio 30 : 70 %wt, 40 : 60 %wt, 50 : 50 %wt, 60 : 40 %wt, 70 : 30 %wt. The next step is the forming process and calcination at a temperature of 900oC with a increase of 10 °C/min. Results of X-Ray Diffraction (XRD) shows that the diffraction peak of SHA/shellac/wheat flour is the value of 2θ: 32.0747º, 33.1943º, 32.5338º. The lowest hardness number of SHA/shellac/wheat flour is 2.86 VHN and the highest is 14.80 VHN, also the highest strong pressure number is 0.20 MPa. The result of microscophy at observation using SEM shows Thar the SHA/shellac/wheat flour 50:50 % wt sample has more porosity as.

Full Text:

PDF

References

N. Akyurt, M. Yetmez, Karacayli, O. Gunduz, S. Agathopoulus, H. Gokce, M. L. Ovecoglu, dan F. N. Oktar, “A New Biomaterial : Sheep Dentine Derived Hydroxyapatite,” Engineering Materials, Vol 493-492, Switzerland, 2012.

Y. Chen, Z. Dong, and X. Miao, “The Effect of Yitria-Stabillized Zirconian on The Properties of the Flourine-Substituted Hydroxyapatite Ceramics Prepared by Pressureless,” J. of Biomimetics, Biomaterial and Tissue Eng., Vol.1, pp. 57-58, 2008.

N. Demirkol, F. Oktar, F. S. Kayali, “Mechanical and Microstructural Properties of Sheep Hydroxyapatit (SHA)-Niobium Oxide Composite.,” Proseedings of the Int. Congress on Advances in Applied Physics and Mater. Sci., Antalya 2011, 2012.

N. Demirkol, F. Oktar, F. S. Kayali, “Influence of Nobium Oxide on the Mechanical Properties of Hydroxyapatite,” Key Engineering Materials, vol. 529-530, pp. 29-30, Switzerland, 2013.

M. Fitriawan, S. R. Amalia, B. A. Saputra, E. Setyawati, A. Yulianto, dan P. M. Aji, “Sintesis Hidroksiapatit Bahan dasar Tulang Sapi dengan Metode Pretipitasi sebagai Kandidat Pengganti Graft Berdasarkan Compressive Strengh,” Prosiding SNMF 2014, Semarang, 2014.

Gunawarman, A. Malik, “Karakteristik Fisik dan Mekanik Tulang Sapi Variasi Berat Hidup Sebagai Referensi Desain Material Implan,” Seminar Nasional Tahunan Teknik Mesin (SNTTM) ke-9, Palembang, 2010.

N. Herdianto, “Studi Bioresorbabilitas Biokeramik Biphasic Calcium Phospate (BCP) Sebagai Material Pengganti Tulang,” Tesis, Universitas Indonesia, Salemba, 2011.

M. K. Herliansyah, D. A. Nasution, M. Hamdi, A. Ide-Ektessabi, M. W. Wildan, A. E. Tontowi, “Preparation and Characterization of Natural Hydroxyapatite : A Comparative Study of Bovine Bone Hydroxyapatite from Calcite,” Material Science Forum, vol. 561- 565, Switzerland, 2007.

M. K. Herliansyah, M. Hamdi, A. Ide-Ektessabi, M. W. Wildan, dan J. A. Toque, “The Influence of Sintering Temperature on The Properties of Compacted Bovine Hydroxyapatite,” Material Science and Engineering, C vol. 29, pp. 1674-1680, 2009.

Majelis Ulama Indonesia., Fatwa., “Penggunaan Shellac sebagai bahan pangan, obat-obatan dan kosmetika,” No. 27, 2013.

I. Sopyan, J. Kaur, “Preparation and Characterization of Pourous Hydroxyapatite through Polymeric Sponge Method,” Ceramics International, vol. 35, pp. 3161-3168, Malaysia, 2009.

Y. C. The, C. Y. Tan, S. Ramesh, J. Purbolaksono, Y. M. Tan, H. Chandran, W. D. Teng dan B. K. Yap “Effect of Calcination on the Sintering Behavior of Hydroxyapatite,” Faculty of Enginering, University of Malaya, 50603, Kualalumpur, Malaysia, 2014.

J. Triyono, S. Susmartini, Susilowati., S. A. Murdiyantara, “Shellac Coated Hydroxyapatite (HA) Scaffold for Increasing Compression Strength,” Advanced Material Researcg, vol. 1123, pp. 378-382, 2015.

DOI: https://doi.org/10.20961/mekanika.v17i2.35125

Refbacks

  • There are currently no refbacks.