MAGNETIC PROPERTIES OF Cu2+ SUBSTITUTED BaFe12-xCuxO19 (x= 0.1,0.2,0.3,..., 4)

Syahrul Humaidi, Ratna A S, Tua Raja S, Seri Dermayu S, Perdamean S


Permanent magnet Barium M-Hexaferrite, BaFe12-x Cux O19  was synthesized with  a wide range of x (x = 0.1, 0.2,  …, 3 and 4mole% respectively). The precursor was made by mixing BaCO3 powder and Fe2O3  powder, whereas CuO powder was used as additive. The powders were mixed together by wet milling in distilled water medium for 20 hours. The powders  had been dried at a temperature of 1000C for 24 h before calcined at a temperature of 11000C for 2 hours. The powders were then grained to prepare 400 mesh (38 µm) in diameter.  The samples density was determined by using Archimedes method, magnetic properties by using permagraph,  crystal structure by XRD-pattern and microwave absorbing properties using VNA. The hysteresis curve showed that the value of magnetic field ranging from  43.36 G to 100.42 G , remanence magnetic induction (Br) 20G-320G, coercivity (HcJ) 1.07 kOe to 9.22 kOe and energy production (BH) max from 0.05kGOe to 0.92 kGOe with a density from 3.82 g/cm3 to 5.2 g/cm3. The  effect of Cu doping tent to increase the value of density with an optimum magnetic properties at  x=0.3%mole.

Full Text:



Cullity, B.D. 1978. Element of X-ray Diffraction. Addison Wesley Publishing

Company. Inc. p 555.

Fiandimas, Arie, 1978. Pembuatan Magnet Permanen Barium Hekasferit berbahan Mill

Scale dengan teknik metalurgi Serbuk. Departemen Fisika, MIPA, Univ. Indonesia.

Ghasemi, A, 2005. “Electromagnetic Properties ang Microwave Absorbing

Characteristic of doped Barium Hexaferrite”. Journal of Magnetism and Magnetic


Gramatyk, P, 2006. “Soft magnetic composite based on nanocrystalline

Fe73.5Cu1Nb3Si13.5B9 and Fe powders”. Journal of Achievement Materials and

Manufacturing Engineering.

Kosasih, A. Noly, 2006. Sintesis Dan Karakterisasi Sifat Magnetik Serbuk Barium M-

Heksaferit Dengan Doping Ion Zn Pada Variasi Temperatur Rendah. Departemen

Fisika, Fakultas Matematika dan Ilmu Pengetahuan Alam, Institut Teknologi Sepuluh

Nopember (ITS).

Iqbal, M.Javed and M.Naeem Ashiq. 2007. “Physical and Electrical Properties of Zr-

Cu Substituted Strontium Hexaferrite Nanoparticles Synthesized by Co-Precipitation

Method”. Chemical Engineering Journal.

Lavina, Wina Indra, 2012. “Pengukuran Densitas Material pada Sampel Padatan dan

Serbuk”. Jurnal Jurusan Fisika Institut Teknologi Sepuluh November Surabaya.

Thompson, J.E 1968. The magnetic of Materials. The Hamlyn Publishing Group Ltd.

Chen Yang Bonded Magnets (Bonded Hard Ferrite and NdFeB Magnets), 2006,

product information, ChenYang Technologies GmbH & Co. KG

T. Koutzarova, S. Kolev, Ch. Ghelev, D. Paneva and I. Nedkov, 2006: phys.stat.

sol.(c) Vol. 3, p. 1302.

Priyono, Arianto,Wibowo dan Nur., 2001, Preparasi Serbuk Barium Ferrite untuk

Menghasilkan Medan Koersive Tinggi : Tinjauan pada Proses Sintering. Vol. 4, No.2,

ISSN : 1410–9662. Hal 45-48.

Sitti Ahmiatri Saptari, Azwar Manaf and Budhy Kurniawan, 2014,


Jurnal Sains Materi Indonesia, Vol. 15, No. 4, Hal : 183,

Sri Dermayu Siregar, 2013, Pengaruh Komposisi CuO Terhadap Penyerap

Gelombang Mikro Pada Pembuatan Magnet Barium Heksaferit (BaFe12-xCuxO19),

Skripsi, Departemen Fisika, FMIPA USU, Medan.


  • There are currently no refbacks.