Pembuatan Ba0,8Sr0,2TiO3 menggunakan Metode Co-precipitation dengan Variasi Suhu Sintering

Isma Alvia Nita, Yofentina Iriani, Fahru Nurosyid

Abstract

Ba0,8Sr0,2TiO3 was made by co-precipitation method with the sintering temperature of 600oC, 700oC, 800oC and 900oC for 4 hours. Sintering temperature was varied to investigate its effect on microstructure and dielectric constant of Ba0,8Sr0,2TiO3. microstructure characterization was performed by X-Ray Diffraction (XRD) instrument. Dielectric constant characterization was perform by LCR meter. The crystal size increased significantly with increasing sintering temperature. Measurements of dielectric constant were performed at range of frequency 0.01 to 100 KHz. Dielectric constant value is highest at the lowest frequency. Dielectric constant value size increased significantly with increasing sintering temperature.

Full Text:

PDF

References

Sunandar, C. (2006). Penumbuhan Film BaxSr1-xTiO3 dan Observasi Sifat Ferroelektriknya. Skripsi, Program Studi Fisika FMIPA IPB.

Dus, B. W., Czekaj, A. L., Orkisz, T., Adamczyk, M., Osinska, K., Kozielski, L & Czekaj, D. (2007). The Sol-Gel Synthesisof Barium Stronsium Titanate Ceramics. Material Science-Poland, 25 (3).

Suasmoro, S., Pratapa, S., Hartanto, D., Setyoko, D. & Dani, U. M. (2000). The Characterization of Mixed Titanate Ba1-xSrxTiO3 Phase Formation from Oxalate Coprecipitated Precursor. Journal of Europian Ceramic Siciety, 20, 309-314.

Khollam, Y. B., Deshpande, S. B., Potdar, H. S., Bhoraskar, S. V., Sainkar, S. R. & Date, S. K. (2005). Simple Oxalate Precursor Route for The Preparation of Barium-Strontium Titanate: Ba1-xSrxTiO3 Powders. Material Latters, 57, 63-74.

Enhessari, M., Parvis, A., Ozaee, K. & Abyanah, H. H. (2011). Synthesis and Characterization of Barium Stronsium Titanate (BST) Micro/nanostructure Prepared by Improved Methods. International Journal of Nano Dimension, 85-103.

DOI: https://doi.org/10.13057/ijap.v7i1.1776

Refbacks

  • There are currently no refbacks.