Nitridasi Plasma Temperatur 423 K pada Permukaan AlMgSi sebagai Bahan Struktur Reaktor Riset

Dwi Priyantoto, Bangun Pribadi, Shokhul Lutfi, Tjito Sujitno

Abstract

Abstract: Nuclear reactors can be divided into research reactors and power reactors. The reactor core containing uranium fuel is where the chain fission reaction takes place. One material that can be used as a fuel structure for research reactors is AlMgSi. One of the characteristics of this alloy is hard. Plasma nitriding method can be used for surface treatment of a metal. The plasma nitriding method at 423 K was used to increase the surface hardness of AlMgSi. Plasma nitriding was carried out with variations of time, namely 2 hours, 3 hours, 4 hours and 5 hours. The results showed that AlMgSi surface hardness after plasma nitridation for 3 hours, rose from 62.35 VHN to 87.65 VHN.

Abstrak: Reaktor nuklir dapat dibedakan menjadi reactor riset dan reactor daya. Teras reactor, berisi bahan bakar uranium adalah tempat berlangsungnya reaksi fisi berantai. Salah satu material yang dapat digunakan sebagai bahan struktur bahan bakar reactor riset adalah AlMgSi. Logam paduan ini salah satu karakteristiknya adalah keras. Metode nitridasi plasma dapat digunakan untuk perlakuan permukaan suatu logam. Dalam penelitian ini metode tersebut digunakan untuk meningkatkan kekerasan permukaan AlMgSi. Nitridasi plasma dilakukan pada temperatur 423 kelvin dengan variasi waktu adalah 2 jam, 3 jam, 4 jam, dan 5 jam. Dari hasil penelitian ditunjukkan bahwa kekerasan permukaan AlMgSi setelah dinitridasi plasma selama 3 jam, naik dari 62,35 VHN menjadi 87,65 VHN.

Keywords

nitridasi plasma; AlMgSi; perlakuan permukaan

Full Text:

PDF

References

Arif, Zuhdi, 2014, “Pengerasan Permukaan Mata Rantai Dengan Plasma Lucutan Pijar DC Dari Campuran Gas Helium Dan Metana”, Tugas Akhir Sekolah Tinggi Teknologi Nuklir BATAN, Yogyakarta.

Aslina Br. Ginting, Supardjo, Yanlinastuti, Dian Anggraini, dan Boybul, 2018, “Karakterisasi Paduan AlMgSi untuk Kelongsong Bahan Bakar U3Si/Al dengan Densitas Uranium 5,2 gU/cm3”, Urania Jurnal Ilmiah Daur Bahan Bakar Nuklir 24 (1), DOI:10.17146/Urania.2018.24.1.4016.

Lutfi, Shokhul, 2015, “Nitridasi Plasma Permukaan AlMgSi sebagai Bahan Struktur Elemen Bakar Reaktor Riset”, Tugas Akhir Sekolah Tinggi Teknologi Nuklir BATAN, Yogyakarta.

Masrukan, 1997, “Paduan AlMgSi1 Sebagai Material Cladding Bahan Bakar Reaktor Riset Alternatif” Prosiding Presentasi llmiah Daur Bahan Bakar Nuklir III PEBN-BATAN Jakarta, tanggal 4-5 Nopember 1997, dengan ISSN 1410-1998.

Priyantoro, Dwi, 2009, “Pengantar Fisika Reaktor Nuklir”, ISBN : 978-979-3984-33-9, Sekolah Tinggi Teknologi Nuklir, BATAN, Yogyakarta.

Sigit dan Elin Nuraini, 1997, “Karakterisasi AlMgSi sebagai Bahan Struktur Reaktor Riset”, Prosiding Presentasi llmiah Daur Bahan Bakar Nuklir III PEBN-BATAN Jakarta, tanggal 4-5 Nopember 1997, dengan ISSN 1410-1998.

Sumpena dan Wardoyo, 2018, “Pengaruh Variasi Temperatur Hardenging dan Tempering Paduan AlMgSi-Fe12% Hasil Pengecoran terhadap Kekerasan’ Jurnal ENGINE Vol. 2 No. 1, Mei 2018, pp no : 26-32; e-ISSN 2579-7433.

DOI: https://doi.org/10.20961/prosidingsnfa.v7i0.71949

Refbacks

  • There are currently no refbacks.