Karakterisasi Struktur Kristal dan Sifat Magnetik Magnet Stronsium Ferit Pasir Besi Batang Sukam Kabupaten Sijunjung Sumatera Barat

Arif Budiman; Dwi Puryanti; Sri Mulyadi Dt. Basa; Muhammad Rizki; Helfi Syukriani

doi:10.20961/prosidingsnfa.v1i0.4500

Prosiding SNFA (Seminar Nasional Fisika dan Aplikasinya)

Karakterisasi Struktur Kristal dan Sifat Magnetik Magnet Stronsium Ferit Pasir Besi Batang Sukam Kabupaten Sijunjung Sumatera Barat

Arif Budiman, Dwi Puryanti, Sri Mulyadi Dt. Basa, Muhammad Rizki, Helfi Syukriani

Abstract

Abstract: The synthesis and characterization of the crystal structure and magnetic properties of strontium ferrite magnets (SrO.6Fe₂O₃) has been done. Hematite (Fe₂O₃) is synthesized from iron sand of Batang Sukam Sijunjung Sumatera Barat through the oxidation process by temperature 700ºC for 3.0 hours. Strontium carbonate (SrCO₃) was obtained from Merck product with a purity of more than 99%. Synthesis of strontium ferrite magnets are made through a process of solid-solid mixing and sintering at a temperature of 1000ºC for 3.0 hours. The results of characterization of X-ray diffraction indicates that it has formed a single phase strontium ferrite magnets with a hexagonal crystal structure. The result of measurement of the magnetic properties shows that an average magnetic susceptibility of strontium ferrite magnet is 266.7 × 10^-8m³ /kg.

Keywords: strontium ferrite magnet, iron sand, crystal structure and magnetic susceptibility.

Abstrak: Telah dilakukan sintesis dan karakterisasi struktur kristal dan sifat magnetik magnet stronsium ferit (SrO.6Fe₂O₃). Hematit (Fe₂O₃) disintesis daripasir besi Batang Sukam Kabupaten Sijunjung Sumatera Barat melalui proses oksidasi dengan temperatur 700ºC selama 3,0 jam. Stronsium karbonat (SrCO₃) diperoleh dari produk Merck dengan kemurnian lebih dari 99 %. Sintesis magnet stronsium ferit dibuat melalui proses solid-solid mixing dan disintering pada suhu 1000ºC selama 3,0 jam. Hasil karakterisasi difraksi sinar-X menunjukkan bahwa telah terbentuk single phase magnet stronsium ferit dengan struktur kristal heksagonal. Hasil pengukuran sifat magnet menunjukkan bahwa magnet stronsium ferit memiliki suseptibilitas magnetik rata-rata 266,7 × 10^-8 m³/kg.

Kata Kunci: magnet stronsium ferit, pasir besi, struktur kristal dan suseptibilitas magnetik.

Full Text:

PDF

References

Cullity, B. D., and Graham, C. D. (2009), Introduction to Magnetic Materials, Second Edition, John Wiley & Sons, Inc., Publication.

Hayati, R. dan Budiman, A. (2016), Karakterisasi Suseptibilitas Magnet Barium Ferit yang Disintesis dari Pasir Besi dan Barium Karbonat Menggunakan Metode Metalurgi Serbuk, Jurnal Fisika Unand (JFU). 4(2); 187-182.

Muljadi, Sardjono, P. dan Sebayang, P. (2013), Analisis Struktur Kristal dan Sifat Magnet SrO.6Fe2O3 Yang Dihasilkan Via Solid-Solid Mixing dan Sintering, Prosiding Pertemuan Ilmiah XXVII HFI Jateng & DIY, Solo, 23 Maret 2013, 111-114.

Norman, F. dan Budiman, A. (2016), Pengaruh Ukuran Butir Pasir Besi Terhadap Kandungan Mineral Magnetik Dan Sifat Magnetik, Studi Kasus: Pasir Besi Pantai Sunur Kabupaten Padang Pariaman Sumatera Barat, Jurnal Fisika Unand (JFU). 4(3); 91-95.

Siregar, S. dan Budiman, A. (2015), Penentuan Nilai Suseptibilitas Mineral Magnetik Pasir Besi Sisa Pendulangan Emas di Kabupaten Sijunjung Sumatera Barat, Jurnal Fisika Unand (JFU). 3(4); 344-349.

Trilismana, H. dan Budiman, A. (2015), Analisis Suseptibilitas magnetik Hasil Oksidasi Magnetit menjadi Hematit Pasir Besi Pantai Sunur Kota Pariaman Sumatera Barat, Jurnal Fisika Unand (JFU). 3(2), 150-156.

Yulianto, S., Bijaksana, S., dan Loeksmanto, W. (2002), Karakterisasi Magnetik Pasir Besi dari Cilacap, Jurnal Fisika Himpunan Fisika Indonesia. A5: 55-60.

DOI: https://doi.org/10.20961/prosidingsnfa.v1i0.4500