Pengaruh Suhu Sintering Pada Pembuatan Strontium Titanat (SrTiO3) Terhadap Konstanta Dielektrik Menggunakan Metode Co-Precipitation

Husnah Rofiko, Yofentina iriani, Risa Suryana

Abstract

Strontium Titanate (SrTiO3) with variation of sintering temperatures were prepared by co-precipitation methods. Sintering temperature were varied at 700oC, 800oC, and 900oC for 4 hours. SrTiO3 samples were prepared by Strontium Nitrate and Titanium Tetrabutoxide. SrTiO3 samples were characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Resistance Capacitance Inductance (RCL) meter, and Sawyer Tower.  SEM images show that the sintering temperatures could affect the grain size of SrTiO3. In addition, crystal size of SrTiO3 (110) affected by sintering temperature. The highest of dielectric constant is 137 on SrTiO3 at sintering temperature of 900oC. Sawyer Tower curves confirmed that SrTiO3 has paraelectric property.

Keyword: Strontium Titanate, Co-precipitation, dielectrics constant, paraelectrics

 

Full Text:

PDF

References

Callister, W.D.. (2007). Materials Science and Engineering An Introduction. The University of Utah: Department of Metallurgical Engineering

Gao, F., Yang, S., Li, J., Qin, M., Zhang, Y.. Sun, H.. (2014). Fabrication, dielectric, and thermoelectric properties of textured SrTiO3 ceramics prepared by RTGG method. Ceramics International 41 (2015)127-135

Goncalves, R.F., Moura, A.P., Godinho, M.J., Longo, E., Machado, M.A.D., De Castro, D.A., Li, M.S.. Marques, A.P.A.. (2014). Crystal growth and photoluminescence of europium-doped strontium titanate prepared by microwave hydrothermal method. Ceramics International

Olivia, W., Faqiang, Z., Feng, L., Yongxiang. (2015). Morphological and phase analysis during the synthesis of Bi7Ti4NbO21 by co-precipitation method. Ceramic International, S41-S46

Zhang, Y., Zhong, Li., Duan, D.. (2015). Single-step hydrothermal synthesis of strontium titanate nanoparticles from crystalline anatase titanium dioxide. Ceramics International 41 (2015) 13516-13524

DOI: https://doi.org/10.13057/ijap.v7i1.1778

Refbacks

  • There are currently no refbacks.